Scientific Reports volume 12, Article number: 20962 (2022) Cite this article 1699 Accesses 2 Citations 5 Altmetric Metrics details Transparent conducting electrodes (TCEs) are essential components in

Scientific Reports volume 12, Article number: 20962 (2022) Cite this article

1699 Accesses

2 Citations

5 Altmetric

Metrics details

Transparent conducting electrodes (TCEs) are essential components in devices such as touch screens, smart windows, and photovoltaics. Metal nanowire networks are promising next-generation TCEs, but best-performing examples rely on expensive metal catalysts (palladium or platinum), vacuum processing, or transfer processes that cannot be scaled. This work demonstrates a metal nanowire TCE fabrication process that focuses on high performance and simple fabrication. Here we combined direct and plating metallization processes on electrospun nanowires. We first directly metallize silver nanowires using reactive silver ink. The silver catalyzes subsequent copper plating to produce Ag–Cu core–shell nanowires and eliminates nanowire junction resistances. The process allows for tunable transmission and sheet resistance properties by adjusting electrospinning and plating time. We demonstrate state-of-the-art, low-haze TCEs using an all-atmospheric process with sheet resistances of 0.33 Ω sq−1 and visible light transmittances of 86% (including the substrate), leading to a Haacke figure of merit of 652 × 10–3 Ω−1. The core–shell nanowire electrode also demonstrates high chemical and bending durability.

Existing and emerging optoelectronic technologies, such as photovoltaics, light-emitting diodes, touch screens, fully transparent displays, and transparent heaters, rely on transparent conducting electrodes (TCEs) to operate. High-performance TCEs optimize two material properties, sheet resistance (Rs) and light transmittance (T), that are difficult to control independently since both depend on the amount of TCE material; greater amounts of TCE material increase Rs and decrease T. The tradeoff between Rs and T is a problem for all TCEs. Optimization of this tradeoff is quantified by a figure of merit (FOM) that combines Rs and T into a single value. The widely used Haacke FOM is equal to T10 Rs−11. Indium Tin Oxide (ITO), the dominant commercial TCE technology, typically achieves Rs of ~ 10 Ω sq−1, ~ 90% T, and a FOM of around 35 × 10–3 Ω−1 (Fig. 1a)2. In addition to relatively low performance, ITO has several other drawbacks that limit applicability and increases cost3: (1) It is brittle in nature, rendering it unsuitable for flexible applications. (2) Indium is increasingly expensive due to its scarcity. (3) ITO deposition usually involves time-consuming and expensive vacuum processes, like magnetron sputtering.

(a) Transmission at 550 nm (T550 nm) as a function of sheet resistance (Rs) plot showing the highest performance nanowire TCEs to date. TCEs based on polymer imprinting22,23,24, electrospinning31,32,33,34,35, and ITO2 are included. The green stars are the highest FOM TCEs from this work for silver nanowires after calcination and silver nanowires with copper plating. The dashed purple lines are Haacke FOM isolines. Some transmittance values were recalculated from their original publications to include comparable substrates (Table S1). (b) Schematic of the TCE fabrication process. 1. An electrospinner deposits polymer nanowires that contain reactive silver ink onto a glass substrate. 2. A hotplate at 300 °C calcines the nanowires for 30 s to vaporize the polymer and reduce the silver precursor. 3. A UV-ozone treatment activates the silver nanowire surface for electroless copper deposition. 4. Electroless copper deposition creates a copper shell around the silver nanowires to fuse the junctions. A core–shell silver–copper nanowire network remains on the substrate. (c) Photograph showing real-world transparency and color neutrality of nanowire TCE.

Researchers have developed a number of strategies to displace incumbent ITO, including TCEs based on metal oxides4,5, carbon nanotubes6,7, graphene8,9, conductive polymers10,11, oxide/metal/oxide strutures12,13,14,15, and metal nanowire networks15,16,17,18,19. Metal nanowire networks are promising due to their high performance, high scalability, low cost, and flexibility20,21. Metals provide unmatched electrical performance, and thin wires are nearly invisible to the human eye at low fill percentages. High-performance metal nanowire TCEs contain low-resistivity wires with uniform distribution and fused junctions to reduce contact resistances. There are various nanowire patterning techniques, including polymer imprinting22,23,24,25, electrohydrodynamic printing26,27, solution processing28,29, cracked film lithography30, and electrospinning31,32,33,34,35,36. Polymer imprinting and electrospinning are two of the most common patterning methods due to their scalability and low cost. Figure 1a provides a survey of some of the highest performance metal nanowire TCEs based on polymer imprinting and electrospinning.

Chen et al. used polymer imprinting to achieve the highest FOM nanowire TCE to date (~ 7800 × 10–3 Ω−1)24. The process involved imprinting high aspect-ratio micro-grooves into a polymer substrate. A secondary electroplating process metallized the grooves. The TCEs produced exhibit extremely high FOMs but are limited to only polymer substrates due to the imprinting process. Furthermore, these TCEs usually have large wires (~ 5 µm), which leads to haze or visible obstruction and less suitability for aesthetic applications, like windows or displays.

Electrospinning is a simple nanowire fabrication process that does not have the same drawbacks as polymer imprinting while still producing some of the highest performance nanowire TCEs (FOM = 762 × 10–3 Ω−1)33. Electrospinning can deposit nanowires onto many substrate materials and produce fine nanowires (< 200 nm diameter), resulting in low haze. Electrospinning uses strong electric fields to accelerate viscous, polymeric solutions from a metal needle onto a collector plate37. The polymer’s viscoelastic properties result in a continuous wire, and the large needle-to-collector distance (~ 10 cm) allows the solvent to evaporate and the wires to draw thin. The result is a randomly distributed network of high-aspect-ratio polymer nanowires.

Two main methods exist for converting electrospun polymer nanowires to conductive metal nanowires: direct metallization31,32 and plating33,38. Direct metallization involves electrospinning a polymer solution that contains metallic precursors. The resulting nanowires are calcined to vaporize the precursor polymers and sinter metallic particles together. Plating involves electrospinning a polymer solution that contains a catalyst, followed by an electroplating or electroless deposition step to plate metal shells around the polymer nanowires. An et al. utilized plating to fabricate the highest-performing electrospun TCE to date (FOM = 762 × 10–3 Ω−1)33. However, their method is quite involved and includes two electrospinning steps, electrodeposition that relies on a platinum catalyst, and transfer from a non-scalable electrically-conductive frame.

In this work, we take a hybrid direct metallization and plating approach to remove expensive materials and simplify the process to fabricate scalable, state-of-the-art nanowire TCEs. We use a simple 4-step process that consists of electrospinning, calcination, surface activation, and electroless copper deposition (Fig. 1b). First, we electrospin a polymer and reactive silver ink solution onto a clean glass substrate, following the Kiremitler et al. procedure31. After electrospinning, a 300 °C hotplate calcines the wires to vaporize the polymers and yield silver nanowires. UV-ozone treatment activates the silver nanowire surface for quicker and more uniform electroless copper deposition. Whereas previous reports use platinum33, palladium38,39, or ruthenium40 catalysts for plating, here, we electrolessly plate copper directly onto the silver nanowires to yield an Ag–Cu core–shell nanowire network. The resultant nanowire network is nearly indistinguishable from bare glass to the naked eye (Fig. 1c). Our highest performing TCEs exhibit a Rs = 0.33 Ω sq−1 and T of 86% (FOM = 652 × 10–3 Ω−1). The result is the second-highest FOM electrospun TCE that we are aware of to date (Fig. 1a) and used processes that are more applicable to commercialization. Our work also represents the first time direct metallization and plating methods have been combined in an electrospun nanowire TCE.

Our nanowire TCE fabrication process focuses on performance and simplified processing. Though prior reports have demonstrated copper plating on silver nanowire seed layers41,42, the present work uniquely forms core–shell structures and targets TCE applications. The process leverages a recent development in direct metallization by Kiremitler et al. who incorporated reactive silver ink into an electrospinning solution31. Replacing traditional particle-based metal inks with reactive inks for direct metallization is advantageous for several reasons, including: (1) higher ink stability, (2) less expensive ink synthesis, and (3) fewer ink contaminants43,44,45. Steps 1 and 2 in Fig. 1b represent the entire Kiremitler et al. process, which is very simple but produces relatively low FOMs (171.6 × 10–3 Ω−1).

We hypothesized that junction resistances were limiting the performance, which an additional electroless deposition step could remedy. This extension to the Kiremitler et al. process resulted in a ~ 2.8 × higher FOM while also increasing the nanowire tunability (Fig. 1a). We chose copper as the electroless plating metal because it is inexpensive and highly conductive. However, other plating metals like silver or nickel should also be effective. The core–shell structure is a result of the two different metallization methods. Ideally, we would electrolessly deposit copper onto the silver nanowires immediately after calcination, but we found that a surface activation step was necessary for more uniform plating (Fig. S1). We chose UV-ozone for the activation step because it is a low-cost and non-vacuum process for improved manufacturability.

Electroless plating contributes to lower Rs in two ways: (1) decreasing the resistance of individual nanowires by increasing their current carrying cross-section and (2) decreasing the contact resistances between nanowires by fusing the junctions. SEM images of nanowire junctions illustrate the junction fusing capability of copper plating (Fig. 2a). The calcined SEM image shows individually stacked silver nanowires with unfused junctions. The copper plating uniformly coats all surfaces and provides a low-resistance path between nanowires. This allows electrons to move through the silver core and copper shell of an individual wire, then transfer between wires through the copper shell. Importantly, all junctions fuse uniformly after copper plating (Fig. 2b). The final nanowires have a width-to-height ratio of ~ 1 (Fig. 2c), with slightly raised junctions due to the stacked wire starting condition (Fig. S2).

(a) SEM images showing nanowire junctions after electrospinning, calcination, and electroless copper plating for 15–120 min. (b) Optical image of a sample after copper plating shows three uniformly fused junctions. (c) Three-dimensional height map of nanowires after copper plating. (d) Plot of nanowire diameter versus plating time. The red line is a linear regression of the data.

Comparing the nanowire growth rate to the decrease in Rs provides evidence that junction fusing is the main contribution of copper plating (Fig. 3a). The formula for resistance of a single nanowire is: r = ρ L A−1, where r is the resistance, ρ is the material resistivity, L is the length, and A is the cross-sectional area. If increasing area were the primary contribution, we would expect a one-to-one relationship between area increase and Rs decrease. However, from calcination to 120 min of copper plating, nanowire cross-sectional area increased by ~ 10 × (diameter increased from ~ 300 to ~ 950 nm, Fig. 2d), whereas Rs decreased by ~ 700 × (244–0.34 Ω sq−1, Fig. 3a). The significant Rs decrease compared to the cross-sectional area increase indicates that cross-sectional area is a minimal contribution of copper plating.

Electrospinning and electroless deposition parameter space investigation. (a) Sheet resistance (Rs) versus copper plating time. (b) Visible Light Transmittance (VLT) versus copper plating time. The dashed green line represents the transmittance of the bare glass substrate. (c) Haacke figure of merit (FOM) versus copper plating time. (d) Optical haze versus plating time.

Electrospinning and electroless plating duration are two of the most impactful fabrication parameters for the Ag–Cu nanowires used in this study. Electrospinning time affects the network density, whereas the plating duration affects the individual wire thicknesses and junction resistances. At the extreme limit, a TCE with low wire density and high plating time can be conceptualized as a single nanowire spanning the substrate, and a TCE with high density and low plating time can be thought of as a continuous thin silver film. The former TCE will have visible wires and poor uniformity, whereas the latter will have low transmittance since all light must pass through a metal layer. To find the optimal conditions for this system, we performed a parameter space investigation with four different electrospinning durations (15–120 s) and five different continuous plating times (0–120 min) (Fig. 3, Table S2). Plating time was limited to 120 min because the copper plating solution homogeneously nucleated copper particles that physisorbed onto the substrate when longer plating times were attempted.

As expected, greater electrospinning times or plating times yielded lower Rs and visible light transmittance (VLT) values. Rs decreased approximately exponentially with plating time, whereas VLT decreased with a near-linear trend in time (Fig. 3a, b). The non-linear Rs decrease shows how junction fusing provided diminishing performance returns. Initially, copper plating rapidly reduced Rs by providing new pathways for electrons to travel. Once the junctions were sufficiently fused, additional plating only improved Rs by increasing the wire’s current carrying cross-sectional area. Larger wires also blocked more photons and decreased VLT. Indeed the linear wire diameter growth rate (Fig. 2d) correlates well with the linear VLT decrease. It is important to note that we report transmittance as VLT, whereas most publications report the transmittance at 550 nm (T550, the wavelength of maximum human eye sensitivity). VLT is advantageous because it weights the entire transmission spectra to the human eye’s sensitivity3,46. Unlike many thin-film oxide-based TCEs, which have wavelength-dependent features due to doping or interference, the transmission spectra of our Ag–Cu core–shell nanowires are nearly flat across the visible spectrum (Fig. S3). As a result, the VLT and T550 values were within 1% for all samples. The flat transmission spectra also result in a color-neutral appearance (Fig. 1c), making these TCEs applicable to aesthetic applications like displays and windows.

The Haacke FOM sharply increased upon initial copper plating due to rapid Rs improvement caused by junction fusing (Fig. 3c). However, the Rs improvement rate decreased as plating continued, and the VLT loss rate remained the same. Additional plating reduced the FOM after a critical point. Greater electrospinning times showed shorter critical plating times. The parameter space investigation yielded a maximum FOM of 652 × 10–3 Ω−1 (Rs = 0.33 Ω sq−1, VLT = 86%) at 30 s of electrospinning followed by 90 min of copper plating. The 652 × 10–3 Ω−1 FOM is a state-of-the-art result for nanowire TCEs, which was fabricated using all-atmospheric fabrication processes and inexpensive materials.

In addition to Rs, VLT, and FOM, haze is an important consideration for TCEs. Low haze (< 3%) is desired for displays and window applications. The haze of Ag–Cu core–shell nanowire arrays tended to increase with greater plating and electrospinning times (Fig. 3d). After calcination, all samples had ≤ 3% haze. After copper plating, the haze increased to a maximum of 3.1, 6.1, 13.6, and 12.6% for samples with 15, 30, 60, and 120 s of electrospinning, respectively. Metal nanowire TCEs are known to exhibit high haze because sub-wavelength features strongly scatter light47. Strategies exist to reduce haze in metal nanowire TCEs48. However, in some applications like photovoltaics, high haze is desirable. Solar cells benefit from top electrodes with high haze because the scattered light increases absorption in the active layer and leads to increased efficiency16,49.

Flexibility is a key advantage of nanowire networks over ITO. ITO performance significantly degrades under bending due to cracks that form under small strains (< 2%)50. These cracks propagate and grow as strain or bending cycles increase51. On the other hand, metal nanowire networks show excellent bending durability16,52,53 due to the ductility of metals and reduced dislocation nucleation and accumulation in nanowires54,55.

We evaluated bending durability of our Ag–Cu core–shell nanowire TCEs by transferring the electrodes onto flexible substrates and conducting bending experiments. The transfer process used clear polypropylene tape to delaminate the electrodes from the glass substrate. Glass substrates that were rigorously cleaned (see Methods) failed to allow delamination of the electrodes due to the strong adhesion between the electrodes and glass. The electrodes showed weaker adhesion to uncleaned glass substrates and enabled the tape transfer process (Fig. 4a). The transferred electrode was subjected to ~ 2.5 mm radius compound bending cycles (Fig. 4b). The compound bend allowed us to evaluate the TCE under compression and tension simultaneously. The resistance increased from 734 to 753 mΩ sq−1 after 1000 bending cycles, which represents a small 2.5% increase in sheet resistance and high bending tolerance (Figs. 4c, S4). 2.5% increase in sheet resistance is comparable to the state-of-the-art for nanowire electrodes under similar bending conditions (Table S3)27,34,39,56,57,58,59.

Mechanical durability evaluation. (a) Photograph of electrode after transferring onto a polypropylene substrate. (b) Photograph of TCE under 2.5 mm radius compound bending. Arrows indicate which areas are under compression and tension. (c) Sheet resistance (Rs) as a function of bending cycles. Sheet resistance increased by 2.5% after 1000 bending cycles.

Chemical durability is a concern for metal nanowire TCEs, especially copper, which is known to oxidize in air. Nanosized metals are reactive in atmospheric oxygen and water because of their large surface-to-volume ratios. Our nanowires and others33,34,60 are between 500 and 1000 nm, which is larger than many literature examples of < 100 nm29,61,62,63. The larger diameter of our materials yields enhanced chemical durability. For instance, 20–40 nm copper nanowires show a 63% increase in sheet resistance after 140 h in air64. Atmospheric degradation of our Ag–Cu core–shell TCEs was investigated by measuring the Rs of each sample six months after fabrication (Table S2). Our > 500 nm diameter nanowires perform significantly better than smaller diameter nanowire electrodes with a typical Rs increase of 4% or less after > 4000 h (6 months). There are a number of strategies to improve the oxidation resistance of copper nanowire electrodes, including encapsulants65,66,67,68,69,70 or surface passivation71,72,73,74,75.

State-of-the-art TCEs (FOM > 650 × 10–3 Ω−1) with broad applicability were fabricated using industrial processes. The novel direct metallization and plating approach begins with electrospinning a polymer and reactive silver ink solution to form silver nanowires. The silver nanowires show high Rs values due to high junction resistances. This work uniquely uses silver nanowires for two roles: (1) as an inexpensive catalyst for electroless copper deposition during device fabrication and (2) to conduct electrical current during device operation. We showed conformal copper coating drastically improved Rs by fusing wire junctions and not by increasing the current carrying area. These Ag–Cu nanowires show class-leading Rs and T while avoiding expensive materials like palladium. Furthermore, adjusting the electrospinning time or the copper deposition duration tunes TCE properties. The high-performance TCE was fabricated using simple processing and demonstrated high chemical and mechanical durability.

We synthesized the electrospinning solution based on the procedure developed by Kiremitler et al.31. The ink has three main constituents: reactive silver ink, two polymers, and water and ethanol as solvents. We made the reactive silver ink and polymer solution separately, then combined them before electrospinning. We made the reactive silver ink following the ink synthesis procedure developed by Walker and Lewis43 and used all chemicals without further purification. First, we weighed 2.00 g of silver acetate (anhydrous 99%, Alfa Aesar) using an analytical balance and added it to a plastic test tube. Next, we added 5.0 ml of ammonium hydroxide (28–30%, ACS grade, Sigma Aldrich) and vortex mixed until the salt was completely dissolved. We then added 0.40 ml of formic acid (≥ 98%, ACS grade, Sigma Aldrich) dropwise over 60 s, vortex mixing between drops. After synthesis, we let the test tubes sit at room temperature for 12 h in a dark environment before filtering the supernatant through a 450 nm syringe filter and storing them at 4 °C until use. We made the polymer solution by mixing 40.0 mg poly(ethylene oxide) (PEO, 900.0 kg/mol Sigma-Aldrich), 50.0 mg polyvinylpyrrolidone (PVP, 1300.0 kg/mol Sigma-Aldrich), 0.5 ml ethanol (100%, Fisher Scientific), and 0.5 ml deionized water in a capped syringe. We used all chemicals as received without further purification. We vortex mixed the syringe for 2 h, then let the solution sit for at least 24 h to allow the polymers to dissolve fully. On the day of electrospinning, we added 1.5 ml of the reactive ink to the syringe mixture and vortex mixed for 30 min. Then we inverted the syringe and let all bubbles rise to the top before attaching a needle to the syringe for electrospinning. By making the solution in the same syringe used for electrospinning, we avoided the possibility of losing constituents when transferring the small volumes between different containers.

We used a lab-built electrospinner (Fig. S5) that consisted of a syringe pump (New Era Pump Systems NE-1010), rotating collector plate (100 rpm), and high voltage supply (ESDEMC ES813-P30.1). We connected the syringe to an 18-gauge needle and connected the needle to the positive output of the high-voltage supply with an alligator clip. We used a flow rate of 0.2 ml/hr, a needle-to-collector distance of 17 cm, and a voltage of 15 kV. The electrospinning duration varied from 15 to 120 s to achieve different wire densities. The substrates were microscope cover glasses (22 mm × 22 mm × 150 µm). Before electrospinning, substrates were cleaned with a 15 min sonication in acetone, then isopropanol, followed by 10 min of UV-ozone cleaning (Setcas, SC-UV-1).

Immediately after electrospinning, we placed each sample on a hotplate at 300 °C for 30 s. Then immediately before electroless deposition, each sample received a 10 s UV-ozone treatment (Setcas, SC-UV-1).

We synthesized an electroless copper plating solution following a recipe developed by Ben Krasnow76. We used all chemicals as received and ensured the previous chemical was fully dissolved before adding the next chemical. First, we added 300 mL of DI water to a beaker with a stir bar and brought it to 40 °C using a hotplate. Then, in order, we added 6.00 g of potassium sodium tartrate tetrahydrate (ACS reagent, 99%, Sigma-Aldrich), 1.50 g copper (II) sulfate pentahydrate (99.995%, Sigma-Aldrich), 1.20 g sodium hydroxide (ACS reagent, ≥ 97%, Sigma-Aldrich), 1.50 g sodium carbonate (ReagentPlus®, ≥ 99.5 Sigma-Aldrich), and 3 ml formaldehyde (ACS reagent, 37 wt.% in H2O, containing 10–15% Methanol as stabilizer, Sigma-Aldrich). During plating, polyimide tape suspended the samples in the solution. A hotplate maintained the bath at 35 °C with no stirring. The deposition time varied from 15 to 120 min. After copper plating, we submerged the samples in two consecutive beakers of DI water to remove excess solution, then blow-dried using compressed nitrogen. We used separate samples for each data point because resubmerging samples in the copper plating solution tended to cause wire delamination.

We measured light transmittance with a visible spectrophotometer (Thermo Scientific, GENESYS 40) over the wavelength range of 325–1100 nm in 1 nm increments. We blanked the spectrophotometer with air, so all transmittance values include the substrate contribution. A custom Python script converted the transmittance spectra to Visible Light Transmittance (VLT). VLT provides a single transmittance value that weights each wavelength according to the human eye's sensitivity. The VLT value was always within 1% of the transmittance at 550 nm. A Varian Cary 5G UV–Vis-NIR Spectrophotometer with an integrating sphere measured the optical haze.

We obtained the sheet resistance by measuring the resistance between two pads separating a square area of TCE material60,77. After fabricating the TCEs, we created silver probing pads along two opposing sides of the samples by airbrushing silver paint, then a 100 °C hotplate cured the silver for ~ 1 min. We removed excess wires so that the pads encompassed an 18 mm × 18 mm square area. We used a source measurement unit (Keysight, B2901A) and a 4-point probe station to collect current–voltage data over the range of 0–10 mA. We calculated the sheet resistance, Rs, using the inverse of the current–voltage slope. Each sample showed an ohmic current–voltage response (Fig. S6).

Bending samples were delaminated using polypropylene tape (Duck® Brand HD Clear™, 66 µm thick). Copper tape contacts, separating an 18 mm × 18 mm square area of the TCE material, were added on opposing sides of the sample (Fig. S4). Alligator clips, connected to the copper contacts, served as connection points to apply bending and measure sheet resistance in situ. A Nordson Pro4L robot pushed and pulled the alligator clips to achieve a 2.5 mm compound bend. Calipers were used to measure the bending diameter at the red arcs indicated in Fig. 4b. An Agilent 34461A digital multimeter, connected to the alligator clips, continually monitored the sheet resistance throughout the bending cycles.

Morphology images were collected with a scanning electron microscope (SEM, Amray 3300 with SEMView 8000 electronics). We used 7 kV accelerating voltage and coated the samples with gold prior to imaging. A laser microscope (Keyence VK-X260K) collected the 3D profile measurements.

The datasets used and/or analyzed during the current study are available from the corresponding author upon reasonable request.

Haacke, G. New figure of merit for transparent conductors. J. Appl. Phys. 47, 4086–4089 (1976).

Article ADS CAS Google Scholar

De, S. & Coleman, J. N. Are there fundamental limitations on the sheet resistance and transmittance of thin graphene films?. ACS Nano 4, 2713–2720 (2010).

Article PubMed CAS Google Scholar

Lee, H. B., Jin, W.-Y., Ovhal, M. M., Kumar, N. & Kang, J.-W. Flexible transparent conducting electrodes based on metal meshes for organic optoelectronic device applications: A review. J. Mater. Chem. C 7, 1087–1110 (2019).

Article CAS Google Scholar

Minami, T. Transparent conducting oxide semiconductors for transparent electrodes. Semicond. Sci. Technol. 20, S35–S44 (2005).

Article ADS CAS Google Scholar

Kang, D. Y. et al. Dopant-tunable ultrathin transparent conductive oxides for efficient energy conversion devices. Nano Micro Lett. 13, 211 (2021).

Article ADS CAS Google Scholar

Jeon, I. et al. High-performance solution-processed double-walled carbon nanotube transparent electrode for perovskite solar cells. Adv. Energy Mater. 9, 1901204 (2019).

Article Google Scholar

Ilatovskii, D. A., Gilshtein, E. P., Glukhova, O. E. & Nasibulin, A. G. Transparent conducting films based on carbon nanotubes: Rational design toward the theoretical limit. Adv. Sci. 9, 2201673 (2022).

Article CAS Google Scholar

Woo, Y. S. Transparent conductive electrodes based on graphene-related materials. Micromachines 10, 13 (2019).

Article Google Scholar

Zhang, H., Mischke, J., Mertin, W. & Bacher, G. Graphene as a transparent conductive electrode in GaN-based LEDs. Materials 15, 2203 (2022).

Article PubMed PubMed Central ADS CAS Google Scholar

Gueye, M. N., Carella, A., Demadrille, R. & Simonato, J.-P. All-polymeric flexible transparent heaters. ACS Appl. Mater. Interfaces 9, 27250–27256 (2017).

Article PubMed CAS Google Scholar

Ouyang, J. Application of intrinsically conducting polymers in flexible electronics. SmartMat 2, 263–285 (2021).

Article CAS Google Scholar

Kim, M. et al. Design of a MoOx/Au/MoOx transparent electrode for high-performance OLEDs. Org. Electron. 36, 61–67 (2016).

Article MathSciNet CAS Google Scholar

Ko, K.-J. et al. Fabrication of an oxide/metal/oxide structured electrode integrated with antireflective film to enhance performance in flexible organic light-emitting diodes. Mater. Today Energy 20, 100704 (2021).

Article CAS Google Scholar

Lee, H. J. et al. Haze-suppressed transparent electrodes using IZO/Ag/IZO nanomesh for highly flexible and efficient blue organic light-emitting diodes. Adv. Opt. Mater. 9, 2002010 (2021).

Article CAS Google Scholar

Nguyen, V. H. et al. Advances in flexible metallic transparent electrodes. Small 18, 2106006 (2022).

Article CAS Google Scholar

Azani, M., Hassanpour, A. & Torres, T. Benefits, problems, and solutions of silver nanowire transparent conductive electrodes in indium tin oxide (ITO)-free flexible solar cells. Adv. Energy Mater. 10, 2002536 (2020).

Article CAS Google Scholar

Yang, Y., Duan, S. & Zhao, H. Advances in constructing silver nanowire-based conductive pathways for flexible and stretchable electronics. Nanoscale 14, 11484–11511 (2022).

Article PubMed CAS Google Scholar

Huang, S. et al. Metal nanowires for transparent conductive electrodes in flexible chromatic devices: A review. Environ. Chem. Lett. 20, 3005–3037 (2022).

Article CAS Google Scholar

Kumar, A., Shaikh, M. O. & Chuang, C.-H. Silver nanowire synthesis and strategies for fabricating transparent conducting electrodes. Nanomaterials 11, 693 (2021).

Article PubMed PubMed Central CAS Google Scholar

Wang, Y., Yokota, T. & Someya, T. Electrospun nanofiber-based soft electronics. NPG Asia Mater. 13, 22 (2021).

Article ADS Google Scholar

Yu, S. et al. Enhanced adhesion of Ag nanowire based transparent conducting electrodes for application in flexible electrochromic devices. Opt. Mater. 120, 111414 (2021).

Article CAS Google Scholar

Khan, A. et al. High-performance flexible transparent electrode with an embedded metal mesh fabricated by cost-effective solution process. Small 12, 3021–3030 (2016).

Article PubMed CAS Google Scholar

Shen, S., Chen, S.-Y., Zhang, D.-Y. & Liu, Y.-H. High-performance composite Ag-Ni mesh based flexible transparent conductive film as multifunctional devices. Opt. Express 26, 27545 (2018).

Article PubMed ADS CAS Google Scholar

Chen, X. et al. Printable high-aspect ratio and high-resolution Cu grid flexible transparent conductive film with figure of merit over 80 000. Adv. Electron. Mater. 5, 1800991 (2019).

Article Google Scholar

Nie, B. et al. High-performance transparent and conductive films with fully enclosed metal mesh. ACS Appl. Mater. Interfaces 13, 40806–40816 (2021).

Article PubMed Google Scholar

Jang, Y., Kim, J. & Byun, D. Invisible metal-grid transparent electrode prepared by electrohydrodynamic (EHD) jet printing. J. Phys. D Appl. Phys. 46, 155103 (2013).

Article ADS Google Scholar

Feng, X. et al. Cost-effective fabrication of uniformly aligned silver nanowire microgrid-based transparent electrodes with higher than 99% transmittance. ACS Appl. Mater. Interfaces 14, 39199–39210 (2022).

Article PubMed CAS Google Scholar

Bai, S., Guo, X., Chen, T., Zhang, Y. & Yang, H. Solution process fabrication of silver nanowire composite transparent conductive films with tunable work function. Thin Solid Films 709, 138096 (2020).

Article ADS CAS Google Scholar

Li, Z. et al. Facile fabrication of large-scale silver nanowire transparent conductive films by screen printing. Mater. Res. Express 9, 066401 (2022).

Article ADS Google Scholar

Muzzillo, C. P., Reese, M. O. & Mansfield, L. M. Fundamentals of using cracked film lithography to pattern transparent conductive metal grids for photovoltaics. Langmuir 36, 4630–4636 (2020).

Article PubMed CAS Google Scholar

Kiremitler, N. B., Esidir, A., Gozutok, Z., Ozdemir, A. T. & Onses, M. S. Rapid fabrication of high-performance transparent electrodes by electrospinning of reactive silver ink containing nanofibers. J. Ind. Eng. Chem. https://doi.org/10.1016/j.jiec.2020.12.010 (2020).

Article Google Scholar

Jang, J. et al. Rapid production of large-area, transparent and stretchable electrodes using metal nanofibers as wirelessly operated wearable heaters. NPG Asia Mater. 9, e432–e432 (2017).

Article CAS Google Scholar

An, S. et al. Self-junctioned copper nanofiber transparent flexible conducting film via electrospinning and electroplating. Adv. Mater. 28, 7149–7154 (2016).

Article PubMed CAS Google Scholar

Bao, C. et al. In situ fabrication of highly conductive metal nanowire networks with high transmittance from deep-ultraviolet to near-infrared. ACS Nano 9, 2502–2509 (2015).

Article PubMed CAS Google Scholar

Wu, H. et al. A transparent electrode based on a metal nanotrough network. Nat. Nanotechnol. 8, 421–425 (2013).

Article PubMed ADS CAS Google Scholar

Woo, H. et al. Highly flexible and transparent film heater with electrospun copper conductive network via junction-free structure. J. Alloys Compd. 886, 161191 (2021).

Article CAS Google Scholar

Teo, W. E. & Ramakrishna, S. A review on electrospinning design and nanofibre assemblies. Nanotechnology 17, R89–R106 (2006).

Article PubMed ADS CAS Google Scholar

Kim, G. H., Shin, J. H., An, T. & Lim, G. Junction-free flat copper nanofiber network-based transparent heater with high transparency, high conductivity, and high temperature. Sci. Rep. 8, 1–8 (2018).

ADS Google Scholar

Testa, A. et al. Transparent flexible electrodes based on junctionless copper nanowire network via selective electroless metallization of electrospun nanofibers. J. Electrochem. Soc. 164, D764 (2017).

Article CAS Google Scholar

Song, J. et al. Fabrication of junction-free Cu nanowire networks via Ru-catalyzed electroless deposition and their application to transparent conducting electrodes. Nanotechnology 33, 065303 (2021).

Article ADS Google Scholar

Wang, Q., Zhang, S., Liu, G., Lin, T. & He, P. The mixture of silver nanowires and nanosilver-coated copper micronflakes for electrically conductive adhesives to achieve high electrical conductivity with low percolation threshold. J. Alloys Compd. 820, 153184 (2020).

Article CAS Google Scholar

Lai, Z. et al. Directly electroplated metallization on flexible substrates based on silver nanowire conductive composite for wearable electronics. ACS Appl. Nano Mater. 4, 12098–12107 (2021).

Article CAS Google Scholar

Walker, S. B. & Lewis, J. A. Reactive silver inks for patterning high-conductivity features at mild temperatures. J. Am. Chem. Soc. 134, 1419–1421 (2012).

Article PubMed CAS Google Scholar

Lefky, C., Mamidanna, A., Huang, Y. & Hildreth, O. Impact of solvent selection and temperature on porosity and resistance of printed self-reducing silver inks: Porosity and resistance of printed self-reducing silver inks. Phys. Status Solidi A 213, 2751–2758 (2016).

Article ADS CAS Google Scholar

Yang, W., List-Kratochvil, E. J. W. & Wang, C. Metal particle-free inks for printed flexible electronics. J. Mater. Chem. C 7, 15098–15117 (2019).

Article CAS Google Scholar

Wheeler, L. M. & Wheeler, V. M. Detailed balance analysis of photovoltaic windows. ACS Energy Lett. 4, 2130–2136 (2019).

Article CAS Google Scholar

van de Groep, J., Spinelli, P. & Polman, A. Transparent conducting silver nanowire networks. Nano Lett. 12, 3138–3144 (2012).

Article PubMed ADS Google Scholar

Kim, S.-W. et al. A full-visible-spectrum invisibility cloak for mesoscopic metal wires. Nano Lett. 18, 3865–3872 (2018).

Article PubMed ADS CAS Google Scholar

Ye, S., Rathmell, A. R., Chen, Z., Stewart, I. E. & Wiley, B. J. Metal nanowire networks: The next generation of transparent conductors. Adv. Mater. 26, 6670–6687 (2014).

Article PubMed CAS Google Scholar

Cairns, D. R. & Crawford, G. P. Electromechanical properties of transparent conducting substrates for flexible electronic displays. Proc. IEEE 93, 1451–1458 (2005).

Article CAS Google Scholar

Alzoubi, K., Hamasha, M. M., Lu, S. & Sammakia, B. Bending fatigue study of sputtered ITO on flexible substrate. J. Displ. Technol. 7, 593–600 (2011).

Article ADS CAS Google Scholar

Hwang, B., Han, Y. & Matteini, P. Bending fatigue behavior of Ag nanowire/Cu thin-film hybrid interconnects for wearable electronics. Facta Universitatis, Series: Mechanical Engineering (2022).

Wang, J.-L., Hassan, M., Liu, J.-W. & Yu, S.-H. Nanowire assemblies for flexible electronic devices: Recent advances and perspectives. Adv. Mater. 30, 1803430 (2018).

Article Google Scholar

Hwang, B., Shin, H.-A.-S., Kim, T., Joo, Y.-C. & Han, S. M. Highly reliable Ag nanowire flexible transparent electrode with mechanically welded junctions. Small 10, 3397–3404 (2014).

Article PubMed CAS Google Scholar

Hwang, B., Kim, T. & Han, S. M. Compression and tension bending fatigue behavior of Ag nanowire network. Extreme Mech. Lett. 8, 266–272 (2016).

Article Google Scholar

Pyo, K. & Kim, J.-W. Thermally stable and flexible transparent heaters based on silver nanowire-colorless polyimide composite electrode. Curr. Appl. Phys. 16, 1453–1458 (2016).

Article ADS Google Scholar

Chae, W. H., Patil, J. J. & Grossman, J. C. Conformal encapsulation of silver nanowire transparent electrodes by nanosized reduced graphene oxide leading to improved all-round stability. ACS Appl. Mater. Interfaces 14, 34997–35009 (2022).

Article PubMed CAS Google Scholar

Hsu, P.-C. et al. Electrolessly deposited electrospun metal nanowire transparent electrodes. J. Am. Chem. Soc. 136, 10593–10596 (2014).

Article PubMed CAS Google Scholar

Mou, Y. et al. Facile preparation of stable reactive silver ink for highly conductive and flexible electrodes. Appl. Surf. Sci. 475, 75–82 (2019).

Article ADS CAS Google Scholar

Hsu, P.-C. et al. Performance enhancement of metal nanowire transparent conducting electrodes by mesoscale metal wires. Nat. Commun. 4, 2522 (2013).

Article PubMed ADS Google Scholar

Wang, H., Wang, Y. & Chen, X. Synthesis of uniform silver nanowires from AgCl seeds for transparent conductive films via spin-coating at variable spin-speed. Colloids Surf. A 565, 154–161 (2019).

Article CAS Google Scholar

Lee, J. H., Huynh-Nguyen, B.-C., Ko, E., Kim, J. H. & Seong, G. H. Fabrication of flexible, transparent silver nanowire electrodes for amperometric detection of hydrogen peroxide. Sens. Actuators B Chem. 224, 789–797 (2016).

Article CAS Google Scholar

Selzer, F. et al. A spray-coating process for highly conductive silver nanowire networks as the transparent top-electrode for small molecule organic photovoltaics. Nanoscale 7, 2777–2783 (2015).

Article PubMed ADS CAS Google Scholar

Ohiienko, O. & Oh, Y.-J. Preparation of narrow copper nanowires with less oxidized surface for flexible and transparent electrodes under octadecylamine. Mater. Chem. Phys. 246, 122783 (2020).

Article CAS Google Scholar

Hong, I. et al. Semipermanent copper nanowire network with an oxidation-proof encapsulation layer. Adv. Mater. Technol. 4, 1800422 (2019).

Article Google Scholar

Celle, C. et al. Oxidation of copper nanowire based transparent electrodes in ambient conditions and their stabilization by encapsulation: Application to transparent film heaters. Nanotechnology 29, 085701 (2018).

Article PubMed ADS Google Scholar

Im, H.-G. et al. Flexible transparent conducting hybrid film using a surface-embedded copper nanowire network: A highly oxidation-resistant copper nanowire electrode for flexible optoelectronics. ACS Nano 8, 10973–10979 (2014).

Article PubMed CAS Google Scholar

Chen, Z., Ye, S., Stewart, I. E. & Wiley, B. J. Copper nanowire networks with transparent oxide shells that prevent oxidation without reducing transmittance. ACS Nano 8, 9673–9679 (2014).

Article PubMed CAS Google Scholar

Yang, J., Bahrami, A., Ding, X., Lehmann, S. & Nielsch, K. Encapsulation of locally welded silver nanowire with water-free ALD-SbOx for flexible thin-film transistors. Appl. Phys. Lett. 121, 163504 (2022).

Article ADS CAS Google Scholar

Bang, J. et al. Advances in protective layer-coating on metal nanowires with enhanced stability and their applications. Appl. Mater. Today 22, 100909 (2021).

Article Google Scholar

Polat Genlik, S. et al. All-solution-processed, oxidation-resistant copper nanowire networks for optoelectronic applications with year-long stability. ACS Appl. Mater. Interfaces 12, 45136–45144 (2020).

Article PubMed CAS Google Scholar

Shi, L. et al. A long-term oxidation barrier for copper nanowires: Graphene says yes. Phys. Chem. Chem. Phys. 17, 4231–4236 (2015).

Article PubMed CAS Google Scholar

Liu, G. et al. Cu nanowires passivated with hexagonal boron nitride: An ultrastable, selectively transparent conductor. ACS Nano 14, 6761–6773 (2020).

Article PubMed CAS Google Scholar

Luo, B. et al. Improved stability of metal nanowires via electron beam irradiation induced surface passivation. ACS Appl. Mater. Interfaces 11, 12195–12201 (2019).

Article PubMed CAS Google Scholar

Choi, S.-G., Seok, H.-J., Kim, J., Kang, J. & Kim, H.-K. Transparent and flexible passivation of MoS2/Ag nanowire with sputtered polytetrafluoroethylene film for high performance flexible heaters. Sci. Rep. 12, 6010 (2022).

Article PubMed PubMed Central ADS CAS Google Scholar

Ben Krasnow. Make plastic printed circuits with a standard laser cutter. https://benkrasnow.blogspot.com/2018/09/make-plastic-printed-circuits-with.html.

Hu, L., Kim, H. S., Lee, J.-Y., Peumans, P. & Cui, Y. Scalable coating and properties of transparent, flexible, silver nanowire electrodes. ACS Nano 4, 2955–2963 (2010).

Article PubMed CAS Google Scholar

Download references

The work was supported by the National Renewable Energy Laboratory, operated by Alliance for Sustainable Energy, LLC, for the U.S. Department of Energy (DOE) under contract No. DE-AC36-08GO28308. Funding was provided by the Building Technologies Office within the U.S. Department of Energy Office of Energy Efficiency and Renewable Energy. The views expressed in the article do not necessarily represent the views of the DOE or the U.S. Government. The U.S. Government retains and the publisher, by accepting the article for publication, acknowledges that the U.S. Government retains a nonexclusive, paid-up, irrevocable, worldwide license to publish or reproduce the published form of this work, or allow others to do so, for U.S. Government purposes.

National Renewable Energy Laboratory, Golden, CO, 80401, USA

Steven J. DiGregorio, Kevin J. Prince & Lance M. Wheeler

Colorado School of Mines, Golden, CO, 80401, USA

Steven J. DiGregorio, Collin E. Miller, Kevin J. Prince & Owen J. Hildreth

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

L.M.W. and S.D. Conceived the work. S.D. and C.E.M. conducted investigation. All authors developed methodology and interpreted data. S.D. and L.M.W. wrote the original draft manuscript. All authors reviewed the manuscript. L.M.W. Acquired funding. L.M.W. and O.J.H. Provided supervision.

Correspondence to Lance M. Wheeler.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

DiGregorio, S.J., Miller, C.E., Prince, K.J. et al. All-atmospheric fabrication of Ag–Cu core–shell nanowire transparent electrodes with Haacke figure of merit >600 × 10–3 Ω−1. Sci Rep 12, 20962 (2022). https://doi.org/10.1038/s41598-022-25080-x

Download citation

Received: 14 August 2022

Accepted: 24 November 2022

Published: 05 December 2022

DOI: https://doi.org/10.1038/s41598-022-25080-x

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.